產(chǎn)品規(guī)格
公稱外徑(mm) | PE80 | PE100 | ||
| SDR17.6 | SDR11 | SDR17.6 | SDR11 | |
| 公稱壓力≦0.2MPa | 公稱壓力≦0.4MPa | 公稱壓力≦0.6MPa | 公稱壓力≦1.0MPa | |
| 壁厚 (mm) | 壁厚 (mm) | 壁厚 (mm) | 壁厚 (mm) | |
| 20 | 2.3 | 3.0 | 2.3 | 3.0 |
| 25 | 2.3 | 3.0 | 2.3 | 3.0 |
| 32 | 2.3 | 3.0 | 2.3 | 3.0 |
| 40 | 2.3 | 3.7 | 2.3 | 3.7 |
| 50 | 2.9 | 4.6 | 2.9 | 4.6 |
| 63 | 3.6 | 5.8 | 3.6 | 5.8 |
| 75 | 4.3 | 6.8 | 4.3 | 6.8 |
| 90 | 5.2 | 8.2 | 5.2 | 8.2 |
| 110 | 6.3 | 10.0 | 6.3 | 10.0 |
| 125 | 7.1 | 11.4 | 7.1 | 11.4 |
| 140 | 8.0 | 12.7 | 8.0 | 12.7 |
| 160 | 9.1 | 14.6 | 9.1 | 14.6 |
| 180 | 10.3 | 16.4 | 10.3 | 16.4 |
| 200 | 11.4 | 18.2 | 11.4 | 18.2 |
| 225 | 12.8 | 20.5 | 12.8 | 20.5 |
| 250 | 14.2 | 22.7 | 14.2 | 22.7 |
| 280 | 15.9 | 25.4 | 15.9 | 25.4 |
| 315 | 17.9 | 28.6 | 17.9 | 28.6 |
| 355 | 20.2 | 32.3 | 20.2 | 32.3 |
| 400 | 22.8 | 36.4 | 22.8 | 36.4 |
| 450 | 25.6 | 40.9 | 25.6 | 40.9 |
| 500 | 28.4 | 45.5 | 28.4 | 45.5 |
| 560 | 31.9 | 50.9 | 31.9 | 50.9 |
| 630 | 35.8 | 57.3 | 35.8 | 57.3 |
性能指標
| 性能 | 要求 |
| 縱向回縮率, %, (110℃) | <=3 |
| 氧化誘導時間, min, (200℃) | >=20 |
| 斷裂伸長率,% | >=350 |
| 炭黑含量（質(zhì)量分數(shù)），%（只適用于黑色混配料） | 2.0~2.5 |
| 溶體流動速率, g/10min (195℃，5kg) | 與產(chǎn)品標稱值的偏差不應超過±20% |
| 耐氣體組分, h(80℃，2Mpa) | ≥20 |
靜液壓強度 1)20℃, 環(huán)向應力:PE100 12.4Mpa, PE809.0Mpa,100h 2)80℃, 環(huán)向應力:PE100 5.4Mpa, PE80 4.5Mpa, 165h 3)80℃, 環(huán)向應力:PE100 5.0Mpa, PE80,4.0Mpa, 1000h |
通過 通過 通過 |
1.無毒。HDPE材質(zhì)無毒無味。
2.低阻流。內(nèi)壁光滑，管道輸送方便，在同等使用環(huán)境下，HDPE管道的輸送能力可提高30%，其粗糙度比鋼管和玻璃纖維增強管小很多。
3. 無泄漏。HDPE管連接的方式有熱熔對接、承插對接和電熔，這意味著連接點的強度比管本身高。
4.靈活性強。小口徑高密度聚乙烯管可以盤管，大口徑管材也可以輕微彎曲，施工更加方便。
5.抗撓性好。HDPE管的耐磨性是鋼管的4倍，這意味著HDPE管道的使用壽命更長，更經(jīng)濟實用。
6.施工方便。PE管可以安裝在各種非開挖工程中，便于施工和安裝。
7.壽命長。在額定溫度和壓力下實用壽命為50年。
8.降低操作和維護成本。高密度聚乙烯管道不僅便于運輸和安裝，而且大大降低了工人的勞動強度，提高了工作效率。
燃氣用埋地聚乙烯管道適用于工作溫度在-20℃ ~~-40℃，長期最大工作壓力不大于0.7MPA的燃氣輸送用管道系統(tǒng)。